Titanium boron agent
|
HT-Ti4OB4
|
Adjust the composition of alloying elements to replace the aluminum intermediate alloy.
|
According to the production of alloy element content in the alloy and the results of the analysis before furnace, calculated at 95% of the recovery efficiency is good, need to add dose, after grilled slag, aluminum evenly dispersed bubble into the molten pool directly, after being small flame disappeared, should be appropriate to strengthen artificial stirring, make its spread evenly, and according to the actual situation, the spread of the guarantee time.
|
The elements are 75% and the silicon is 95%.
The yield is greater than 95%.
The solid yield of iron agent is over 90%.
Shelf life is one year.
|
Temperature: 740 ℃ to 760 ℃.
Melt time: 15 to 30 minutes.
|
1, 500 g/piece
Density: 3.8-4.2 kg/cm after
Si: 2.5 g/cm after
|