name：HT - Mn75 manganese agent

time：2018-11-3 15:13:03

Introduction

HT - Mn75 manganese agent
I. purpose:
Adjust the content of manganese in different aluminum alloy to replace the intermediate alloy and reduce the melting temperature.
Ⅱ. Product features:
1. Element content 75%
2. The yield is greater than 95%
3. Direct input, easy to use.
Ⅲ. Usage:
According to the content of alloying element in the alloy plate and the analysis results before the furnace, the required dosage (quantity of Mn agent) is calculated according to the actual yield of 90%. After the slag is scraped, it is directly distributed and thrown into the aluminum melting pool. After the small flame disappears, manual stirring should be strengthened to make it spread evenly, and a certain diffusion time should be guaranteed according to the actual situation.
Ⅳ. Process parameters:
1, using temperature: 740-760 ℃
2. Amount of addition (kg) = (alloy element composition (%) - pre-furnace analysis of the element content)
3. Melting time: 15-30 minutes
Ⅴ. packaging and storage:
Of the goods
model
use
Method of use
The characteristics of
The process parameters
specifications
Titanium boron agent
HT - Ti4OB4
Adjust the composition of alloying elements to replace the aluminum intermediate alloy.
According to the production of alloy element content in the alloy and the results of the analysis before furnace, calculated at 95% of the recovery efficiency is good, need to add dose, after grilled slag, aluminum evenly dispersed bubble into the molten pool directly, after being small flame disappeared, should be appropriate to strengthen artificial stirring, make its spread evenly, and according to the actual situation, the spread of the guarantee time.
The elements are 75% and the silicon is 95%.
The yield is greater than 95%.
The solid yield of iron agent is over 90%.
Shelf life is one year.
Temperature: 740 ℃ to 760 ℃.
Melt time: 15 to 30 minutes.
1, 500 g/piece
Density: 3.8-4.2 kg/cm after
Si: 2.5 g/cm after
Titanium agent
HT - Ti75
Manganese agent
HT - Mn75
Copper agent
HT - Cu75
iron
HT - Fe75
Chromium agent
HT - Cr75
Nickel agent
HT - Ni75
zinc
HT - Zn75
Fast solvent
HT - Si95

PREV：HT - Fe75 iron
NEXT：HT-Ni75 nickel additive

go back

RELATED NEWS

Guess you're interested

+86-0516-83892255/+86-0516-83882188

Home

Products

About us

News

Job

Contact us

name：HT - Mn75 manganese agent

RELATED NEWS

Navigation：

Contact us

Search